Package of semiconductor device and its manufacturing method

ABSTRACT

A packaged semiconductor device structure comprises a semiconductor chip ( 20 ) having a bump electrode ( 5 ), a facing substrate ( 9 ) having on one face thereof a facing electrode ( 8 ) contacting an end face of the bump electrode ( 5 ) and a bonding agent ( 7 ) filled in between the semiconductor chip ( 20 ) and the facing substrate ( 9 ). The bump electrode ( 5 ) is of a double layer structure composed of a core part ( 5   b ) and a convex-shaped electrode end part ( 5   a ) fabricated above the core part ( 5   b ) separately from the core part.

TECHNICAL FIELD

[0001] This invention relates to a packaged semiconductor device structure configured so that a semiconductor chip having a bump electrode is mounted on a facing wiring substrate, and a method for fabricating the packaged semiconductor device structure.

BACKGROUND ART

[0002] In Japanese Patent Applications Laid-open Nos. 4-82241 and 11-284022, there is disclosed a technology of mounting a semiconductor element having a bump electrode on a facing wiring substrate in such a way that a thermosetting bonding insulating resin is filled in between the semiconductor element and the wiring substrate to press the bump electrode of the semiconductor element against the wiring substrate so that the wiring substrate and an electrode on the wiring substrate are subjected to plastic or elastic deformation into a concave shape to ensure that the semiconductor element is electrically connected to the electrode on the wiring substrate. The bump electrode of the above semiconductor element is one deposited on a pad electrode of the semiconductor element using a metal material such as Au by electroplating or the like.

[0003] An approach to deposition of the bump electrode as described above fails to adjust a tip end shape of the bump electrode. Thus, with the bump electrode pressed against the wiring substrate, the tip end shape of the bump electrode is not sufficiently in agreement with a shape of the electrode on the wiring substrate deformed by being pressed against the bump electrode, so that stabled electric connection is sometimes unattainable.

DISCLOSURE OF THE INVENTION

[0004] An object of the present invention is to provide a packaged semiconductor device structure, which is highly reliable in mounting a semiconductor chip having a bump electrode to a facing substrate having on a surface thereof a facing electrode to ensure that sufficient electric connection between the bump electrode and the facing electrode is attainable without damaging the facing electrode, and a method for fabricating the above packaged semiconductor device structure as well.

[0005] In order to attain the above object, a packaged semiconductor device structure according to the present invention comprises a semiconductor chip having a bump electrode; a resin-made facing substrate having on one face thereof a facing electrode contacting an end face of the above bump electrode; and an insulating, thermoplastic or thermosetting or photo-curing bonding agent filled in between the semiconductor chip and the facing substrate. In addition, the bump electrode is of a double-layer structure composed of a core part and a convex-shaped electrode end part fabricated on the core part separately from the core part.

[0006] The electrode end part composing the bump electrode may be rounded dependent on an amount of a material of the electrode end part by heating this electrode end part material, and is thus easily adjustable to suit properties of materials of the facing substrate and the facing electrode. Thus, sure electric connection between the bump electrode and the facing electrode is attainable.

BRIEF DESCRIPTION OF THE DRAWINGS

[0007]FIG. 1 is a cross-sectional view showing a packaged semiconductor device structure according to a first embodiment of the present invention;

[0008]FIG. 2 is a cross-sectional view showing a packaged semiconductor device structure according to a second embodiment of the present invention;

[0009]FIGS. 3A to 3D are views illustrating a method for fabricating the packaged semiconductor device structure shown in FIG. 1;

[0010]FIGS. 4A to 4D are views illustrating a method for fabricating the packaged semiconductor device structure shown in FIG. 2, specifically, a process up to a point at which a bump electrode having a step-like pattern is obtained in the course of fabrication of the packaged semiconductor device structure; and

[0011]FIGS. 5A to 5C are views illustrating a method for fabricating the packaged semiconductor device structure shown in FIG. 2, specifically, a process from deposition of the bump electrode having the step-like pattern to deposition of an electrode end part and an electrode coating on the bump electrode.

BEST MODE FOR CARRYING OUT THE INVENTION

[0012] A first embodiment of a packaged semiconductor device structure according to the present invention will now be described with reference to FIGS. 1 and 3A to 3D.

[0013] In FIG. 1, a silicon single crystal substrate 1 of about 0.3 mm to 1.0 mm in thickness has thereon a semiconductor integrated circuit such as an active element, a logic circuit and a circuit interconnection. The substrate 1 is to configure a semiconductor chip 20, in cooperation with a pad electrode 2 and a passivation 3 respectively on the substrate 1. The pad electrode 2 is to connect a power source and/or a signal-related interconnection of the semiconductor integrated circuit on the substrate 1 to the outside. The passivation 3 has an opening at a portion facing the pad electrode 2, and is effective in protecting the semiconductor integrated circuit on the substrate 1.

[0014] In addition, the pad electrode 2 and the passivation 3 around the outside of the pad electrode have thereon a bump electrode 5. The bump electrode 5 has an upper end face whose center part is protruded into a rounded convex shape (partial spherical shape).

[0015] The bump electrode 5 on the semiconductor chip 20 is electrically connected to a facing electrode 8 of a resin-made facing substrate 9 with an insulating bonding agent 7 filled in between the semiconductor chip 20 and the facing substrate 9. With the bump electrode 5 electrically connected to the facing electrode 8, the facing substrate 9 is in a concavely deformed condition so as to be fitted with the convex-shaped upper end face of the bump electrode 5, as shown in FIG. 1.

[0016] In fabrication of a packaged structure of FIG. 1, either of the semiconductor chip 20 or the facing substrate 9 is firstly coated with an insulating bonding agent 7. Next, the bump electrode 5 on the semiconductor chip 20 is adhered to the facing electrode 8 on the facing substrate 9 under conditions of pressure bonding by heating so as to allow low pressure bonding stress to be held for a certain period of time at temperatures equal to or less than a glass transition temperature (Tg) of a material of the facing substrate 9, specifically, at which the insulating bonding agent 7 becomes hardened. Adhesion of the bump electrode 5 to the facing electrode 8 as described above allows the facing substrate 9 and the facing electrode 8 to be deformed so as to have a concave part in conformity with the convex-shaped end face of the bump electrode 5. As a result, the semiconductor chip 20 is electrically connected to the facing electrode 8 through engagement of the convex-shaped end face of the bump electrode 5 with the concave part on the facing electrode 8.

[0017] In deposition of the bump electrode 5, a core layer 5 b is firstly deposited on an upper surface of a barrier metal layer 4, and thereafter, an electrode end part 5 a is deposited on the core layer. A metal material having a melting point higher than that of the electrode end part 5 a is used for the core layer 5 b. Selective melting applied to the electrode end part 5 a ensures that surface tension of molten metal thereof allows the end face of the bump electrode 5 to be deformed into an approximately partial spherical shape. Even if the electrode end part 5 a having a spherical surface whose radius of curvature is increased leads to insufficient height of the bump electrode 5, the bump electrode 5 is adjustable in height so as to meet a required height by increasing a thickness of the core layer 5 b.

[0018] In addition, the bump electrode 5 may also have on an uppermost layer thereof a bump electrode coating 5 c. The bump electrode coating 5 c is effective in preventing the surface of the bump electrode 5 from being oxidized, and also of ensuring satisfactory connection to the facing electrode 8.

[0019] The electrode end part 5 a of the bump electrode 5 preferably needs to use a material having an elasticity modulus higher than that of the material of the facing substrate 9 and also having a melting point higher than Tg of the material of the facing substrate 9. For instance, highly conductive metals such as Au, Ag, Sn, Ni and Pb and plastics containing these metals are available. When the bump electrode 5 having the electrode end part 5 a formed with the above material is subjected to heating and pressure bonding to the facing substrate 9 under the above conditions of pressure bonding by heating, a pressure bonding stress applied to the facing electrode 8 is appropriately dispersed in such a way as to be absorbed by the facing substrate 9 to ensure that the facing substrate 9 is plastically deformed so as to have the concave part. As a result, the bump electrode 5, with its shape maintained, may attain satisfactory electric connection to the facing electrode 8. The facing substrate 9 having the concave part whose depth is set as much as about 5 μm is effective in compensating for height variations of the bump electrode 5 in the range of 1 to 2 μm, even if the above variations occurred.

[0020] The facing substrate 9 preferably needs to use a thermoplastic or thermosetting resin material excellent in insulation and smoothness or the like, and more preferably, a resin composition having Tg lower than the melting point of the material used for the bump electrode 5. For instance, a thin sheet or a film that consists of thermoplastic resin such as polycarbonate, polyethersulfone and liquid crystal polymer or thermosetting resin such as epoxy and polyimide is available. These resin materials may be optionally added with fillers or covered with a gas barrier layer.

[0021] For easy deformation of the facing substrate 9 and the facing electrode 8 so as to have the concave part in conformity with the end face shape (convex shape) of the bump electrode 5, the facing electrode 8 preferably needs to use a single-layered or multi-layered film material consisting of highly conductive and/or elongate-able metal such as Al, Cu, Ni and Au of 10 μm or less in thickness or a composition containing these metals, more preferably, a multi-layered film obtained by depositing an Au film of 1 μm or less in thickness on an upper layer of a Cu film of 10 μm or less in thickness.

[0022] Further, in a transparent electrode used for a liquid crystal display, an indium tin oxide (which will be hereinafter simply referred to as ITO) film of 1 μm or less in thickness is preferably used for the facing electrode. Further, when the above ITO film is used, an upper layer thereof may have a single-layered or multi-layered film consisting of metal such as Al, Cu and Au of 1 μm or less in thickness or a composition containing these metals.

[0023] With considerations of bonding the semiconductor chip 20 to the facing substrate 9, the insulating bonding agent 7 preferably needs to use a material that may be sufficiently hardened under the conditions of pressure bonding by heating at temperatures equal to or less than a melting point of the bump electrode 5, specifically, equal to or less than Tg of the material of the facing substrate 9. Thus, the material of the insulating bonding agent 7 may include a thermoplastic or thermosetting or photo-curing resin composition, preferably, a thermosetting resin composition that may be hardened within a range of temperatures equal to or less than Tg of the facing substrate 9. For instance, a resin composition such as acrylic, urethane or epoxy resin is preferably available.

[0024] In bonding the semiconductor chip 20 to the facing substrate 9, the process of firstly coating either of the semiconductor chip 20 or the facing substrate 9 with the insulating bonding agent 7 in advance of subjecting the bump electrode 5 of the semiconductor chip 20 to heating and pressure bonding to the facing substrate 9 has been described. Alternatively, the above bonding may also take place in such a way as to allow the insulating bonding agent 7 to be filled and hardened after pressure bonding of the bump electrode 5 to the facing electrode 8.

[0025] In addition, the pad electrode 2 of the semiconductor chip 20 and the bump electrode 5 may also have therebetween a barrier metal layer 4 that is effective in preventing the metal materials of the pad electrode 2 and the bump electrode 5 from mutual diffusion.

[0026] An embodiment of a method for fabricating the packaged semiconductor device structure of FIG. 1 will now be described with reference to FIGS. 3A to 3D.

[0027] 1. Process to Deposit the Core Layer and the Electrode End Part of the Bump Electrode on the Pad Electrode on the Substrate (See FIG. 3A)

[0028] The silicon single crystal substrate 1 has thereon the pad electrode 2 and the passivation 3 that are to compose the semiconductor chip. The passivation 3 is opened to ensure that only the surface of the pad electrode 2 is bared.

[0029] Firstly, the barrier metal layer 4 consisting of a Ti/W composition film of 0.5 μm in thickness is deposited by sputtering over the whole surface region including the passivation 3 and the pad electrode 2. Then, a plating resist coating 10 is deposited by photolithography on an upper surface region of the barrier metal layer 4, except for an upper part of the pad electrode 2.

[0030] Then, the core layer 5 b is deposited on the barrier metal layer 4 above the pad electrode 2 with no plating resist coating 10 thereon in such a way as to allow Cu of 20 μm in thickness to be grown by electroplating using the barrier metal layer 4 as a common electrode film.

[0031] Further, the electrode end part 5 a is deposited in such a way as to allow metal having a melting point lower than that of the core layer 5 b, specifically, solder with Sn-to-Pb ratios of 6:4, to be grown by electroplating using the barrier metal layer 4 as the common electrode film.

[0032] With the above process, a structure as shown in FIG. 3A is obtained.

[0033] 2. Process to Deform the End Face (Face Contacting the Facing Electrode) of the Bump Electrode into a Convex Shape (Approximately Partial Spherical Shape) (See FIG. 3B):

[0034] Firstly, the silicon single crystal substrate 1 is allowed to stand for 20 seconds on a hot plate having a temperature of 200° C. Then, heat transmitted from the silicon single crystal substrate 1 causes only the electrode end part 5 a of the bump electrode 5 to be melted to ensure that the surface tension of the molten electrode end part 5 a allows the electrode end part 5 a to be deformed into an approximately partial spherical shape. A radius of curvature of the spherical surface of the electrode end part 5 a is easily adjustable depending on an amount of metal plating to be grown. Specifically, a decrease in metal plating amount increases the radius of curvature, thereby providing the electrode end part 5 a having a gently rounded end face. On one hand, an increase in metal plating amount increases the height of the electrode end part 5, but decreases the radius of curvature of the end face of the bump electrode 5.

[0035] Further, the bump electrode coating 5 c consisting of Au of 0.1 μm in thickness is deposited on the surface of the electrode end part 5 a in a growing manner by electroplating.

[0036] With the above process, a structure as shown in FIG. 3B is obtained.

[0037] 3. Process to Fabricate the Semiconductor Chip Having the Bump Electrode (See FIG. 3C):

[0038] Firstly, the plating resist coating 10 of the structure shown in FIG. 3B is stripped using a commercially available resist stripper to bare the barrier metal layer 4 to the outside.

[0039] Then, the bared barrier metal layer 4 is etched with a hydrogen peroxide solution.

[0040] With the above process, a structure as shown in FIG. 3C is obtained.

[0041] 4. Process to Electrically Connect the Bump Electrode 5 to the Facing Electrode 8 (See FIG. 3D):

[0042] Firstly, the ITO of 0.8 μm in thickness is deposited by sputtering on the facing substrate 9 consisting of polycarbonate resin of 0.2 mm in thickness to obtain the facing electrode 8 of a desired pattern by photolithography.

[0043] Further, the insulating bonding agent 7 consisting of an unhardened epoxy resin composition is supplied to a surface (surface to be packaged) of the facing substrate 9.

[0044] Next, the bump electrode 5 of the semiconductor chip (composed of the pad electrode 2 and the passivation 3) is slowly subjected to heating and pressure bonding to the facing electrode 8 on the facing substrate 9 at pressures of 40 Kg/cm² at 130° C., and then its bonded condition is maintained for 2 minutes. As a result, the facing substrate 9 and the facing electrode 8 are deformed so as to have the concave part in conformity with the tip end shape of the bump electrode 5. Then, sure electric connection between both the electrodes 5 and 8 is attainable through engagement of the convex-shaped (partially spherical-shaped) bump electrode 5 with the concave part of the facing electrode 8.

[0045] Simultaneously with the above pressure bonding, the semiconductor chip (composed of the pad electrode 2 and the passivation 3) is firmly bonded to the facing substrate 9 in such a way as to allow the insulating bonding agent 7 to be sufficiently hardened.

[0046] With the above process, the packaged structure shown in FIG. 1 is completely fabricated.

[0047] The bump electrode 5 of the packaged structure according to the present invention has the end face taking the shape of a partial spherical surface, and also ensures that the unhardened insulating bonding agent 7 in between contact faces of both the electrodes 5 and 8 is easily ejected therefrom in an initial stage of the process of subjecting the bump electrode 5 on the semiconductor chip to heating and pressure bonding to the facing electrode 8 on the facing substrate 9. As a result, the contact faces of both the electrodes 5 and 8 may be connected together directly (without being filled with the bonding agent 7).

[0048] In the above embodiment, supply of the unhardened insulating bonding agent 7 of the epoxy resin composition to the surface (surface to be packaged) of the facing substrate 9 takes place in advance of allowing the bump electrode 5 on the semiconductor chip to be adhered to the facing electrode 8 on the facing substrate 9. Alternatively, adhesion of the bump electrode 5 on the semiconductor chip to the facing electrode 8 on the facing substrate 9 may also take place in advance of supplying the unhardened liquid-state insulating bonding agent 7 to between the semiconductor chip and the facing substrate 9 in a dispensing manner, and the process of subjecting the semiconductor chip to heating and pressure bonding to the facing substrate 9 follows to allow both the electrodes 5 and 8 to be connected together.

[0049] In fabrication of the packaged semiconductor device structure according to the method of the present invention, satisfactory electric connection is also attainable even under low temperature or low pressure bonding stress conditions. Thus, when the packaged semiconductor device structure according to the present invention is mounted on the resin-made facing substrate 9, damages to the facing electrode on the facing substrate 9 may be minimized. Thus, according to the present invention, it is possible to provide a packaged semiconductor device structure adaptable to packaging of high density.

[0050] A second embodiment of a packaged semiconductor device structure of the present invention will now be described with reference to FIGS. 2, 4A to 4C and 5A to 5C.

[0051] The packaged semiconductor device structure shown in FIG. 2 has the bump electrode 5 whose core layer 5 b has a step-like pattern, differently from the packaged structure of FIG. 1. The following will give a description on a method for fabricating the packaged structure of the second embodiment.

[0052] 1. Process to Deposit the Core Layer of the Bump Electrode on the Pad Electrode of the Substrate (See FIG. 4A):

[0053] The same manner as that used for fabrication of the packaged structure of FIG. 1 is employed to deposit the electrode 2, the passiavation 3, the barrier metal layer 4 and the core layer 5 b.

[0054] Specifically, the barrier metal layer 4 is deposited by sputtering over the whole surface region including the passivation 3 and the pad electrode 2. Then, the plating resist coating (not shown in FIG. 4A) is deposited by photolithography on an upper surface region of the barrier metal layer 4 except for an upper part of the pad electrode 2. Then, the core layer 5 b is deposited on the barrier metal layer 4 above the pad electrode 2 with no plating resist coating thereon in such a way as to allow Cu of 20 μm in thickness to be grown by electroplating using the barrier metal layer 4 as the common electrode film. Further, the plating resist coating is stripped using a resist stripper, and a bared portion (specifically, a portion covered with no core layer 5 b) of the barrier metal 4 is etched with the hydrogen peroxide solution, thereby providing a structure as shown in FIG. 4A.

[0055] 2. Process to Deposit the Plating Resist Coating (See FIG. 4B):

[0056] The plating resist coating 10 is deposited on the passivation 3 and the core layer 5 b in such a way as to newly coat the structure of FIG. 4A with positive resist by spin coating, thereby providing a structure as shown in FIG. 4B.

[0057] 3. Process to Obtain a Step-Like Resist Pattern (See FIG. 4C)

[0058] The plating resist coating 10 in the structure shown in FIG. 4B is etched with a photolithography mask (not shown) consisting of a Cr material. Specifically, irradiation of ultraviolet rays from an exposure light source to the photolithography mask takes place to control decomposition of the resist depending on the extent of a quantity of ultraviolet rays for patterning as follows. That is, a first region 10 a of the plating resist coating 10 is eliminated by etching to ensure that the core layer 5 b is completely bared to the outside. A second region 10 b thereof is etched halfway to ensure that the core layer 5 b is covered with the plating resist coating 10 of a small thickness. A third region 10 c thereof is assigned as a region subjected to no etching.

[0059] It is noted that the above first and second regions 10 a and 10 b are regions above the core layer 5 b, and the third region 10 c is a region out of an upper part position of the core layer 5 b.

[0060] 4. Process to Subject the Core Layer to Etching (See FIG. 5A):

[0061] The structure shown in FIG. 4C is subjected to dry etching. With this dry etching, etching of the core layer 5 b in the first region 10 a with the core layer 5 b bared to the outside is started from the initial stage of dry etching, while etching of the core layer 5 b in the second region 10 b covered with the plating resist coating 10 of the small thickness is started after the plating resist coating 10 of the small thickness is eliminates by dry etching.

[0062] A structure having the step-like core layer 5 b as shown in FIG. 5A is obtained through the above dry etching.

[0063] The structure shown in FIG. 5A has the core layer 5 b of two steps. Alternatively, for the core layer 5 b of three or more steps, use of a photolithography mask having a pattern for varying a quantity of ultraviolet rays shielded in three or more levels is only needed.

[0064] 5. Process to Deposit the Electrode End Part on the Step-Like Core Layer (See FIG. 5B):

[0065] As shown in FIG. 5B, the electrode end part 5 a is deposited in an isotropic growing manner by electroplating.

[0066] 6. Process to Deposit the Bump Electrode Coating (See FIG. 5C):

[0067] After the electrode end part 5 a of the step-like core layer is rounded by the same heat treatment as that in the first embodiment, the bump electrode coating 5 c is deposited thereon by electroplating, thereby providing a structure as shown in FIG. 5C.

[0068] As described above, according to the present invention, the bump electrode on the semiconductor chip is of a two layer structure composed of the core layer and the electrode end part, so that the tip end of the electrode end part on the semiconductor chip may be formed in an arbitrary rounded shape, and is also easily adjustable to suit properties of the materials of the facing substrate and the facing electrode. Thus, sure electric connection between the bump electrode and the facing electrode is attainable.

[0069] As long as the gently rounded face of the electrode end part 5 a is placed on the input side of the facing electrode 8, the damages to the input side of the facing electrode 8 in fabrication of the packaged structure may be minimized. Even if the facing electrode 8 opposite to the input side is damaged, there is no problem in driving of the semiconductor device. Thus, the present structure is considered to be one adaptable to packaging of further increased density, and besides, particularly effective in coping with a case where there is a possibility that damages to the bump electrode 8 are attributable to the materials or the like of the facing substrate 9 and the facing electrode. 

1. A packaged semiconductor device structure, comprising; a semiconductor chip having a bump electrode; a resin-made facing substrate having on one face thereof a facing electrode contacting an end face of said bump electrode; and an insulating, thermoplastic or thermosetting or photo-curing bonding agent filled in between said semiconductor chip and said facing substrate; wherein said bump electrode is composed of a core part and a convex-shaped electrode end part fabricated on said core part separately from said core part.
 2. The packaged semiconductor device structure according to claim 1, wherein the electrode end part of said bump electrode has thereon a bump electrode coating that is effective in preventing a surface of said bump electrode from being oxidized and also of ensuring satisfactory connection to said facing electrode.
 3. The packaged semiconductor device structure according to claim 1, wherein a pad electrode composing said semiconductor chip and the core part of said bump electrode have therebetween an electrode film that is effective in allowing said core part to be grown by electroplating.
 4. The packaged semiconductor device structure according to claim 1, wherein the core part of said bump electrode has a step-like pattern having two or three or more steps.
 5. A method for fabricating a packaged semiconductor device structure, comprising: depositing a core part of a bump electrode on a pad electrode of a semiconductor chip; depositing an electrode end part of the bump electrode on a surface of said core part in such a way as to allow a metal material having a melting point lower than that of said core part to be grown by a predetermined amount by plating: heating said semiconductor chip to cause only the electrode end part of said bump electrode to be melted to ensure that the electrode end part is rounded dependent on a quantity of the metal material having been used for the electrode end part; supplying an unhardened insulating bonding agent to a surface to be packaged of the facing electrode or the semiconductor chip; subjecting the bump electrode on said semiconductor chip to heating and pressure bonding to the facing electrode on the facing substrate, and then maintaining the bonded condition for a predetermined period of time to ensure that the facing substrate and the facing electrode are deformed so as to have a concave part and that both the electrodes are electrically connected together through engagement of the concave part of the facing electrode with the electrode end part of the bump electrode; and bonding firmly said semiconductor chip to said facing substrate in such a way as to allow said insulating bonding agent to be sufficiently hardened, while maintaining the above condition.
 6. A method for fabricating a packaged semiconductor device structure, comprising: depositing a barrier metal layer on a surface of a semiconductor chip by sputtering, and then depositing a plating resist coating on an upper layer region of said barrier metal layer except for an upper part of a pad electrode composing said semiconductor chip; depositing a core part of a bump electrode on an upper surface of the barrier metal layer on said pad electrode with no plating resist coating thereon in such a way as to allow a predetermined metal to be grown by electroplating using said barrier metal layer as an electrode film; depositing an electrode end part of the bump electrode in such a way as to allow metal solder having a melting point lower than that of said core part to be grown by a predetermined amount by electroplating; allowing a substrate mounted with said semiconductor chip to stand on a heated hot plate for a predetermined period of time to cause only the electrode end part of said bump electrode to be melted with heat transmitted from said substrate to ensure that the electrode end part is rounded dependent on an amount of the metal solder having been used for the electrode end part; stripping the plating resist coating using a resist stripper to bare the barrier metal layer to the outside, and then etching the bared barrier metal layer; supplying an unhardened insulating bonding agent to a surface to be packaged of the facing substrate or the semiconductor chip; subjecting the bump electrode on said semiconductor chip to heating and pressure bonding to the facing electrode on the facing substrate and then maintaining the bonded condition for a predetermined period of time to ensure that the facing substrate and the facing electrode are deformed so as to have a concave part and that both the electrodes are electrically connected together through engagement of the concave part of the facing electrode with the electrode end part of the bump electrode; and bonding said semiconductor chip to said facing substrate in such a way as to allow said insulating bonding agent to be hardened.
 7. A method for fabricating a bump electrode of a semiconductor chip, comprising: depositing a core part of a bump electrode on a pad electrode composing a semiconductor chip; depositing a plating resist coating on the semiconductor chip in a region including said core part; allowing the plating resist coating on said core part to have multi-thickness levels in such a way as to vary a quantity of light radiation in multiple levels when etching takes place with a photolithography mask applied to said plating resist coating; allowing said core part to have a step-like pattern in such a way as to subject the plating resist coating having said multi-thickness levels to dry etching; allowing an electrode end part to be grown on said step-like patterned core part by plating; rounding said electrode end part by reflow-process; and depositing an electrode coating on said electrode end part by plating. 